期刊
JOURNAL OF MEMBRANE SCIENCE
卷 610, 期 -, 页码 -出版社
ELSEVIER
DOI: 10.1016/j.memsci.2020.118262
关键词
Leaf ZIFs; Troger's base polymer; Mixed matrix membranes; Hydrogen separation
资金
- Research Council of Norway [254791]
In this work, two two-dimensional (2D) leaf ZIFs (ZIF-L-Zn and ZIF-L-Co) were incorporated into the Troger's base (TB)-based polymers for hydrogen separation. SEM imaging and enhanced performance have demonstrated good dispersion of leaf ZIFs in the resultant mixed matrix membranes (MMMs), thanks to the good compatibility between polymeric matrix and nanoleaves. The addition of both leaf ZIFs greatly enhances the gas permeabilities of all investigated species within the studied loading. Due to the interlayer channels in the laminated 2D ZIFs, small molecules like H-2 obtain additional fast transport pathway and, thus, a remarkable increase in gas permeability up to 4 times. A H-2 permeability of 1235.5 Barrer was achieved in the presence of 20 wt% ZIF-L-Co. Compared with ZIF-L-Zn, ZIF-L-Co is more efficient in promoting gas permeabilites with similar selectivities for all gas pairs. The MMMs with ZIF-L-Co have displayed excellent hydrogen separation performances, which surpass all Upper Bounds of H-2/CO2, H-2/N-2 and H-2/CH4. Further increasing the operating temperature enhances the gas transport properties, and the membrane with 20 wt% ZIF-L-Co at 60 degrees C gives a H-2 permeability up to 1985.9 Barrer, which is 6.8 times greater than that of the neat polymer membrane at room temperature.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据