JOURNAL OF ALLOYS AND COMPOUNDS
卷 823, 期 -, 页码 -出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2020.153763
关键词
Metals and alloys; Mechanical properties; Microstructure; Dislocations and disclinations; Scanning electron microscopy
资金
- Science and Engineering Research Board, Department of Science and Technology, India
Deformation behaviour of FCC CoCuFeMnNi single phase high entropy alloy (HEA) was studied under quasistatic and dynamic loading conditions in compression at strain rate of 0.001 s(-1) and 3000 s(-1) using screw driven universal testing machine and split Hopkinson pressure bar respectively. A detailed microstructural characterization was carried out using electron back scatter diffraction (EBSD) while bulk texture measurement was carried out using X-ray diffraction. The high strain rate deformed sample shows high strain rate hardening as well as higher strain hardening that is attributed to operation of deformation twinning as observed from EBSD. The operation of deformation twinning and multiple slip systems leads to grain fragmentation and weakening of characteristic < 101 > compression texture in sample subjected to high strain rate. Constitutive behaviour of the CoCuFeMnNi HEA explained using the Johnson-Cook model further justifies better strain rate and strain hardening response of the alloy compared to individual elements. (C) 2020 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据