JOURNAL OF ALLOYS AND COMPOUNDS
卷 821, 期 -, 页码 -出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2019.153259
关键词
Nickel-based alloy; Aging; Long needle-like carbide; Without gamma ' phase; Toughness
资金
- National Key Research and Development Plan [2017YFB0305201]
This work aims to study the differences in the microstructure and mechanical properties of a new nickel-based alloy without gamma' phase during long-term aging at 675 degrees C. The test alloy C-HRA-2 for next-generation power plant applications was simulated for 5000 h at the service temperature. The formation of long needle-like M23C6 carbides inside the grains is a unique phenomenon compared to conventional nickel-based alloys. After aging for 500 h, the microstructure, strength and hardness tend to be stable, while the toughness shows a slow downward trend. Even so, the toughness still exceeds 110 J after aging for 5000 h. Compared with the alloy 617/617B containing the gamma' phase, the strength of the alloy without gamma' phase (C-HRA-2) reduced by about 5-10%, and the hardness lowered by 5-15%, but the elongation also increased by about 10-50%, and the toughness increased by about two times. (C) 2019 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据