The Ba1-xSrxMg2V2O8 (0 <= x <= 0.4) microwave dielectric ceramics were fabricated by a standard solid-state reaction method. The formation of a continuous solid solution within the whole composition range was identified. The ceramic samples could be well densified in the temperature range of 885-975 degrees C in air for 4 h. The permittivity er was found to increase with increasing ionic polarizabilities. The Qxf values were believed to be closely related with packing fraction and grain refinement. The Sr2+ substitution contributed to a monotonous increase of the A-site bond valence, such that the tau(f) value experienced a considerable variation from negative to positive values. The optimum microwave dielectric properties of an epsilon(r) of 13.3, a high Qxf of 86,640 GHz (9.6 Hz) and a near-zero tau(f) of -6 ppm/degrees C could be yielded in the x=0.15 sample when sintered at 915 degrees C for 4 h. (C) 2016 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据