CERAMICS INTERNATIONAL
卷 42, 期 2, 页码 3666-3672出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2015.11.034
关键词
Powders: chemical preparation; Dielectric properties; Magnetic properties; Ferrites; Soft magnets
CoFe2-2xLixCuxO4 (x=0.00, 0.05, 0.1, 0.15, 0.2, 0.25) spinel ferrite nanoparticles have been synthesized using a CTAB assisted hydrothermal method. Structural characterization of the ferrite powders was carried out using X-ray diffraction (XRD) and scanning electron microscopy (SEM). Employing X-ray diffraction analysis, the synthesized samples were found to be in single crystalline phase with crystallite size of 25 29 nm. The microstructural analysis revealed that the shape of particles can be changed considerably by selecting proper content of the dopants. The room temperature resistivity of all the doped samples was observed to decrease with increase in Li-Cu doping up to a value of 1.9 x 10(6) Omega cm. The dielectric measurements showed the normal Maxwell Wagner type dielectric dispersion due to interfacial polarization. The optimum values of saturation magnetization (M-s), remnant magnetization (M-r) and coercivity (H-c) were found as 46 emu/g, 12 emu/g and 284 Oe respectively for Li-Cu content of x=0.10. (C) 2015 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据