Silicon; flame retardancy; smoke suppression; synergy; carbon layer
资金
- National Natural Science Foundation of China [51302183]
- Key Research and Development Program Projects in Shanxi Province [2017030321015-4]
- Natural Science Foundation of Shanxi Province [201801D121096, 2012021021-6]
To reduce the environmental hazard from the flame retardant, a halogen-free phosphorus-containing silicone flame-retardant poly N,N dimethylene phosphate aminopropyl siloxane (PDPSI) was prepared following the Mannich reaction. Then, PDPSI and ferric oxide (Fe2O3) were used for the preparation of synergistic flame-retardant polyethylene terephthalate (PET). The flame-retardant test results revealed that at 2% PDPSI/Fe2O3 content and 1:2 mass ratio of PDPSI to Fe2O3, the limit oxygen index value of the PDPSI/Fe2O3/PET composite material was 27.9%, reaching the flame-retardant level and passing the V-0 rating in the UL-94 test. In addition, the PDPSI/Fe2O3/PET composites had a char residue content of 17.5% at 700 degrees C, an increase of 30.6% compared to that of the pristine PET. In the cone calorimeter test, the addition of PDPSI/Fe2O3 significantly reduced the peak heat release rate (PHRR), total heat release (THR) rate, and total smoke production (TSP) value of the resulting PET composites. PHRR and THR decreased by 66.05% and 14.3%, respectively. The TSP value decreased from 14.4 m(2) to 8.1 m(2), a decrease of 43.8%. The scanning electron microscopy images and Fourier-transform infrared spectra of the char residue showed a significant synergy between Fe2O3 and PDPSI, changing the structure of the carbon layer in continuous and dense form, thus the flame retardancy and smoke suppression of the PET composites improved. In addition, the tensile strength of the PET composite was 42.11 MPa, which was only 1.84% less than that of the pristine PET.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据