关键词
Lead-free BCZT ceramics; Plasma Activated Sintering; Structure; Dielectric property and ferroelectric property
资金
- National Natural Science Foundation of China [51272195, 51521001]
- 111 project [B13035]
- Hubei Provincial National Natural Science Foundation [2015CFB724]
Lead-free Ba0.85Ca0.15Zr0.10Ti0.90O3 (BCZT) ceramics were prepared by Plasma Activated Sintering (PAS). The influence of PAS sintering temperature on the crystalline phase, microstructure, and, dielectric and ferroelectric properties of BCZT ceramics were studied. The phase structure of BCZT ceramics first changed from rhombohedral phase to the coexistence of rhombohedral and tetragonal phases and then to tetragonal phase as the sintering temperature increased. Microstructural characterization of BCZT ceramics indicated that PAS can obtain a compact microstructure at lower temperatures of 1150-1300 degrees C compared with that from common pressureless sintering. The BCZT ceramics showed different degrees of diffuseness with increased temperature, and the diffuseness exponents C are all approximately on the order of 10(5) degrees C. The dielectric and ferroelectric properties of BCZT ceramics were enhanced with increased sintering temperature. BCZT ceramics sintered at 1250 degrees C exhibited optimum properties of room temperature epsilon(r)=2863, epsilon(m)=6650, and 2P(r)=25.24 mu C/cm(2), resulting from the relatively higher tetragonal phase content of the MPB between tetragonal and rhombohedral phases together with a compact microstructure. (C) 2016 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据