期刊
CERAMICS INTERNATIONAL
卷 42, 期 12, 页码 13368-13377出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2016.05.088
关键词
Seebeck effect; Cobaltites; Chemical route; Thermal conductivity
资金
- Universidad Nacional de Colombia, Medellin Campus [17362]
The physical transport properties of layered 112-type YBaCo2O5+delta cobaltites, synthesized via non-ion selective EDTA-citrate-metal complexing, were systematically investigated by means of electrical and thermal conductivity as well as through thermopower measurements. The transport properties were shown to be markedly dependent on the oxygen content delta. The temperature dependence of the thermopower, S(T), exhibits p-type conductivity in the temperature range 60-320 K. In the low-temperature antiferromagnetic region, S(T) exhibits an unusual behavior (broad peak), which can be explained by the electron magnon scattering mechanism. The temperature dependence of the thermal conductivity exhibits a glass-like behavior, and no thermal conductivity peak can be seen at low temperatures for any of the samples. The absence of the phonon peak at low temperatures is associated with the oxygen non-stoichiometry, which brings about strong lattice disorder. The calculated figure of merit (ZT) shows values (similar to 10(-5) at room temperature) too small for applications, as expected from 112-type cobaltite systems. (C) 2016 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据