Unlike the common high temperature pyrolysis of carboxymethylcellulose (CMC) targeting activated carbon, this study investigates the pyrolytic behaviour of plain CMC at low temperatures ranging between 260 and 300 A degrees C. Preliminary experiments were conducted using differential scanning calorimetry to define the temperature range necessary for the process. Low-temperature pyrolysis was then simulated using thermogravimetric analysis under inert atmosphere. Investigations reveal that a minimum holding temperature of 260 A degrees C is required for an isothermal process, at which pyrolysis is terminated after around 26 min. Increasing exposure temperature reduces pyrolysis time. Within the range of the investigated sample and CMC particle size, no significant effects could be measured regarding the decomposition behaviour. The resulting char was further analysed using X-ray diffraction and Fourier transform infrared spectroscopy. Visual inspection was conducted using scanning electron microscopy. Upon pyrolysis, originally longitudinally shaped CMC was found to be converted into spherical particles of functionalised amorphous carbon with an average particle size of 41 A mu m.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据