COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING
卷 132, 期 -, 页码 -出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.compositesa.2020.105799
关键词
3-Dimensional reinforcement; Microstructures; Chemical analysis; Prepreg processing
资金
- Major State Basic Research Development Program of China [2015CB655200]
- National Natural Science Foundation of China [11672087]
The need for combined high-temperature insulation and load-bearing functions under large temperature gradient conditions imposes new demands on functionally graded composite materials. Herein, a ceramic-polymer continuous gradient composite was prepared by a polymer-derived ceramic route using a custom-designed induction heating system. The gradient composite was subjected to six impregnation-crosslinking-pyrolysis cycles to obtain a 55-mm-long gradient layer with varying density (1.76-1.43 g/cm(3)). The compositions of the gradient matrix varied from amorphous SiCN ceramics to silicon resin from top to bottom, satisfying the gradient change rule. The gradient material had good thermal insulation and reusability with a heat flux of 0.3 MW/m(2) for 10 min. The resin layer has the minimum compressive strength of 68 MPa. This material could serve as transition material for connecting a high-temperature zone (>= 1000 degrees C) with a low-temperature one (<= 350 degrees C).
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据