Nano-MgO; Resin composite; Antibacterial property; Compressive strength; Wear resistance
资金
- National Natural Science Foundation of China [51703106]
- Natural Science Foundation of Shandong Province of China [ZR2016EMQ05]
A new type of photocurable resin composite containing nano-MgO was synthesized in order to reduce the occurrence of secondary caries. Different mass ratios (0 %, 1 %, 2 %, 4 %, 8 %) of nano-MgO were added into resin composites. The antibacterial properties of nano-MgO powder and modified resin composites against Streptococcus mutans (S. mutans) were detected by antibacterial ring test and film contact test, respectively. Compressive strength (CS) and wear resistance were determined by a universal testing machine and an abrasion test machine. The results indicated that antibacterial activity and wear resistance of resin composites containing nano-MgO were superior to the control group (p < 0.05). The antibacterial rate reached as high as 99.4 % when the mass ratio of nano-MgO was 8 %. However, the CS values tended to decline as the content of nano-MgO increase. Hence, the addition of nano-MgO showed excellent antibacterial property to resin composites and enhanced wear resistance, but was detrimental to their mechanical properties.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据