Bi2Te3; diffusion barrier; shear strength; fracture mode; thermoelectric properties; interfacial stability
资金
- Ministry of Science and Technology of Taiwan [107-2221-E-008-004-MY3]
- Industrial Technology Research Institute of Taiwan
Bismuth telluride (Bi2Te3)-based thermoelectric materials are well-known for their high figure-of-merit (zT value) in the low-temperature region. Stable joints in the module are essential for creating a reliable device for long-term applications. This study used electroless Co-P to prevent a severe interfacial reaction between the joints of solder and Bi2Te3. A thick and brittle SnTe intermetallic compound layer was successfully inhibited. The strength of the joints improved, and the fracture mode became more ductile; furthermore, there was no significant degradation of thermoelectric properties after depositing the Co-P layer after long-term aging. The result suggests that electroless Co-P could enhance the interfacial stability of the joints and be an effective diffusion barrier for Bi2Te3 thermoelectric modules.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据