期刊
ACS APPLIED MATERIALS & INTERFACES
卷 12, 期 15, 页码 17314-17320出版社
AMER CHEMICAL SOC
DOI: 10.1021/acsami.0c03478
关键词
polycaprolactones; multiarmed; tissue adhesive
资金
- U.S.-Israel Binational Science Foundation (BSF) [2015182]
Existing tissue adhesives have a trade-off between adhesive strength and biocompatibility. Here, we report a series of biocompatible multiarmed polycaprolactones (PCL) as tissue adhesives that can be released from a hot glue gun and the length of each arm was kept at similar to 2-3 kg mol(-1) in all the polymers. The adhesion properties were dependent on the number of functionalized (N-hydroxysuccinimide ester (NHS), aldehyde (CHO), and isocyanate (NCO)) arms of the multiarmed polymers. The more arms, the higher the adhesion strength. For example, the adhesion strength in binding cut rat skin increased from 2.3 N cm(-2) for 2PCL-NHS to 11.2 N cm(-2) for 8-PCL-NHS. CHO- and NCO-modified 8PCL also had suitable adhesive properties. All the multiarmed polymers had minimal cytotoxicity in vitro and good biocompatibility in vivo, suggesting their potential as promising alternative surgical adhesives.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据