ACS APPLIED MATERIALS & INTERFACES
卷 12, 期 14, 页码 17070-17076出版社
AMER CHEMICAL SOC
DOI: 10.1021/acsami.0c00763
关键词
femtosecond laser; perovskite; blue shift; asymmetric response; optoelectronic device
资金
- National Natural Science Foundation of China [11704028]
- National Key R&D Program of China [2017YFB1104300]
We have explored an asymmetric optoelectronic response of an FAPb(I0.8Br0.2)(3) (FA = formamidine) perovskite device irradiated by a femtosecond (fs) laser at different laser-fluence values. Photoluminescence (PL) spectra indicated a blue shift from 772 nm (1.606 eV) to 745 nm (1.664 eV) and more than 80% quenching of the irradiated perovskite. The blue shift of the PL spectra can be attributed to compositional variation, which was confirmed through elemental analysis and X-ray diffraction. Two distinct characteristic time constants 193-46 ps and 1.9-0.61 ns were obtained by using fs transient absorption spectroscopy. The fast one represents recombination at the interface, whereas the slow one represents band-to-band recombination in the interior of the grain. Interestingly, after the perovskite was irradiated by a femtosecond laser with an appropriate laser fluence (0.135 J/cm(2)), an asymmetric I-V characteristic was achieved, which should result from irreversible electric domain deflection. Due to the electron-phonon scattering induced by defects, the degree of asymmetry was sensitive to the illumination power. As the photosensitive asymmetric I-V characteristics have a bearing on its photoelectric properties, the findings would be of value in photodiode, memory, and other photoelectric devices.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据