Mg-Gd-Y-Zr; Heat treatment; High temperature tensile property; Anomalous temperature dependence
资金
- National Natural Science Foundation of China [51771115, 51775334]
- National Science and Technology Major Project [2017ZX04006001]
- Joint Fund for Space Science and Technology [6141B06300401, 6141B06310106]
- Science Innovation Foundation of Shanghai Academy of Spaceflight Technology [SAST2016048]
The aim of this work is firstly to optimize T6 heat-treatment of low-pressure sand-cast Mg-10Gd-3Y-0.5Zr alloy, and then systematically investigate the mechanical behavior of the T6-treated alloy from room temperature to 300 degrees C. It turned out that the optimum T6 heat-treatments for the tested alloy are 525 degrees C x 12h + 225 degrees C x 14h and 525 degrees C x 12h + 250 degrees C x 12h which integrated age-hardening and tensile properties into account, respectively. The strength of the T6-treated alloy indicates obvious anomalous temperature dependence from room temperature to 300 degrees C, namely both ultimate tensile strength and yield strength of the tested alloy firstly increase with tensile temperature, and then decrease as temperature increases further. Elongation increased with temperature monotonously. The tensile fracture mode of the tested alloy changes from transgranular fracture to intergranular fracture with the increasing of test temperature. (C) 2019 Published by Elsevier B.V. on behalf of Chongqing University.