卷 9, 期 1, 页码 45-54出版社
SPRINGEROPEN
DOI: 10.1007/s40145-019-0346-0
关键词
Mn2+ red-emitting; YAG:Ce, Mn transparent ceramics; white light-emitting diodes (WLEDs) application; low color temperature
资金
- CAS Priority Research program [XDB20010300, XDA21010204]
- National Natural Science Foundation of China [201501178]
- Natural Science Foundation of Fujian Province [2017H0048]
A series of YAG:Ce,Mn transparent ceramics were prepared via a solid-state reaction-vacuum sintering method. The effects of various Mn2+-Si4+ pair doping levels on the structure, transmittance, and luminescence properties were systematically investigated. These transparent ceramics have average grain sizes of 10-16 mu m, clean grain boundaries, and excellent transmittance up to 83.4% at 800 nm. Under the excitation of 460 nm, three obvious emission peaks appear at 533, 590, and 745 nm, which can be assigned to the transition 5d -> 4f of Ce (3+) and T-4(1)->(6)A(1) of Mn2+. Thus, the Mn2+-Si4+ pairs can effectively modulate the emission spectrum by compensating broad orange-red and red spectrum component to yield high quality warm white light. After the optimized YAG:Ce,Mn transparent ceramic packaged with blue light-emitting diode (LED) chips, correlated color temperature (CCT) as low as 3723 K and luminous efficiency (LE) as high as 96.54 lm/W were achieved, implying a very promising candidate for application in white light-emitting diodes (WLEDs) industry.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据