关键词
PEDOT:PSS; organic devices; spin coating; doctor blade coating; spray coating; thermographic camera
资金
- Polish National Center of Research and Development [TECHMATSTRATEG1/347431/14/NCBR/2018]
Poly(3,4-ethylenedioxythiophene:poly(styrenesulfonate) (PEDOT:PSS) water and toluene solutions were investigated in detail, taking into consideration their stability, wettability, transparency, and electrochemical properties, along with change polarity caused by dopant. As dopant, methanol, ethanol, and isopropanol were used with different dipole moments (1.70, 1.69, and 1.66 D) and dielectric constants (33.0, 24.5, and 18.0). Three techniques, i.e., spin coating, doctor blade coating, and spray coating, were employed to created PEDOT:PSS layers on glass, glass/indium tin oxide (ITO), and glass/fluorine-doped tin oxide (FTO) substrates with optimized technical parameters for each used equipment. All used PEDOT:PSS water and toluene solutions demonstrated good wetting properties with angles below 30 degrees for all used surfaces. Values of the energy bandgap (Eg) of PEDOT:PSS investigated by cyclic voltammetry (CV) in solution showed increase energy Eg along with addition of alcohol to the mixture, and they were found in the range of 1.20 eV to 2.85 eV. The opposite tendency was found for the Eg value of the PEDOT:PSS layer created from water solution. The storage effect on PEDOT:PSS layers detected by CV affected only the lowest unoccupied molecular orbital (LUMO) level, thereby causing changes in the energy bandgap. Finally, simple devices were constructed and investigated by infrared (IR) thermographic camera to investigate the surface defects on the created PEDOT:PSS layers. Our study showed that a more stable PEDOT:PSS layer without pin-holes and defects can be obtained from water and toluene solutions with isopropanol via the spin coating technique with an optimal speed of 3000 rpm and time of 90 s.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据