Mg-based bulk metallic glass; biodegradable; surface roughness; osteogenetic
类别
资金
- Ministry of Science and Technology of Taiwan [MOST 108-2218-E-038-001]
- Taipei Medical University within Ministry of Education in Taiwan [DP2-108-21121-01-O-02]
Mg-based bulk metallic glass materials have been investigated for their large potential for application in orthopedic implants due to their biocompatibility, low degradation rate, and osteogenetic ability. As an orthopedic implant, initial cell adhesion has been a critical issue for subsequent osteogenesis and bone formation because the first contact between cells and the implant occurs upon the implants surface. Here, we aimed to create Mg-based bulk metallic glass samples with three different surface roughness attributes in order to understand the degradation behavior of Mg-based bulk metallic glass and the adhesion ability and osteogenetic ability of the contact cells. It was found that the degradation behavior of Mg66Zn29Ca5 bulk metallic glass was not affected by surface roughness. The surface of the Mg66Zn29Ca5 bulk metallic glass samples polished via #800 grade sandpaper was found to offer a well-attached surface and to provide a good cell viability environment for Human MG63 osteoblast-like cell line. In parallel, more calcium and mineral deposition was investigated on extracellular matrix with higher surface roughness that verify the relationship between surface roughness and cell performance.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据