Mn-Ce-Ti-O composite aerogel; mesopore size; NH3-SCR; apparent activation energy; SO2 resistance
类别
资金
- National Natural Science Foundation of China [U1710252]
Novel Mn-Ce-Ti-O composite aerogels with large mesopore size were prepared via a one-pot sol-gel method by using propylene oxide as a network gel inducer and ethyl acetoacetate as a complexing agent. The effect of calcination temperature (400, 500, 600, and 700 degrees C) on the NH3-selective catalytic reduction (SCR) performance of the obtained Mn-Ce-Ti-O composite aerogels was investigated. The results show that the Mn-Ce-Ti-O catalyst calcined at 600 degrees C exhibits the highest NH3-SCR activity and lowest apparent activation energy due to its most abundant Lewis acid sites and best reducibility. The NO conversion of the MCTO-600 catalyst maintains 100% at 200 degrees C in the presence of 100 ppm SO2, showing the superior resistance to SO2 poisoning as compared with the MnOx-CeO2-TiO2 catalysts reported the literature. This should be mainly attributed to its large mesopore sizes with an average pore size of 32 nm and abundant Lewis acid sites. The former fact facilitates the decomposition of NH4HSO4, and the latter fact reduces vapor pressure of NH3. The NH3-SCR process on the MCTO-600 catalyst follows both the Eley-Rideal (E-R) mechanism and the Langmuir-Hinshelwood (L-H) mechanism.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据