Partial shading; Reverse bias; CIGS; Wormlike defects; Propagation mechanism; TCO
资金
- 'Netherlands Enterprise Agency' (RVO)
- Dutch Topteam Energy [TEID215005, TEUE116203]
- Early Research Program 'Sustainability & Reliability for solar and other (opto-)electronic thin-film devices' from TNO
Partial shading of monolithically interconnected Cu(In,Ga)Se-2 (CIGSe) modules can lead to the formation of reverse bias induced defects. These localized defects permanently reduce the output of the PV module. The formation and propagation mechanisms of these defects is studied. Understanding these mechanisms can help to prevent or mitigate damage due to partial shading of CIGSe PV modules. A propagation mechanism is proposed based on both compositional changes found at the edges of the reverse bias induced defects and differences in observed propagation patterns caused by the lateral voltage drop over the TCO layer.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据