期刊
NANOTECHNOLOGY
卷 31, 期 21, 页码 -出版社
IOP PUBLISHING LTD
DOI: 10.1088/1361-6528/ab7250
关键词
all-inorganic perovskite; CsPbBr3 nano-spheres; fluorescence blinking; surface defect state; surface passivation
资金
- National Natural Science Foundation of China [91750103, 11674343, 11474297, U1531109]
- Youth Innovation Promotion Association CAS [2016221]
- Shanghai Committee of Science and Technology [17ZR1444000]
We demonstrated strong fluorescence blinking on large all-inorganic perovskite (CsPbBr3) nano-spheres. By performing (time-resolved) micro-photoluminescence (mu-PL) measurements, the unique blinking characteristics of the as-grown nano-spheres with diameters of hundred nanometers, are clearly observed. Blinking has no obvious on/off states, which is different from the blinking characteristics of quantum dots. It is believed that the blinking of fluorescence is caused by metastable defect-induced trapping of carriers on the surface of the nano-spheres, because dramatically suppressed fluorescence blinking and the decay rates of ultrafast carriers are realized by surface passivation of the nano-spheres. Surface defects are closely related to the ambient atmosphere, which has been further confirmed by PL measurements of the as-grown nano-spheres in vacuum. Additionally, we also found that the fluorescence blinking was significantly suppressed as the sample size increased, which can be attributed to the large-size induced average effect on fluorescence blinking. These results may be important for understanding the mechanism of the fluorescence blinking of perovskite materials and for developing optical devices with good fluorescence stability.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据