期刊
MICROPOROUS AND MESOPOROUS MATERIALS
卷 293, 期 -, 页码 -出版社
ELSEVIER
DOI: 10.1016/j.micromeso.2019.109796
关键词
3-D graphene; N-doped porous carbon; Covalent cross-linking; Supercapacitors
类别
资金
- Key Basic Research Program of Hebei Province of China [17964402D, 18964408D]
A 3-D covalently crosslinked N-doped porous carbon/holey graphene composite (NPC/HG) was synthesized by carbonizing the precursor mixture of casein, graphene oxide (GO) and KOH. The polypeptide and amino acid produced by hydrolysis of casein in KOH solution could react with GO, which was conducive to the uniform coating of the NPC precursor on GO and the mutual crosslinking of GO. After carbonization, NPC with a high specific surface area was uniformly coated in the two-dimensional plane of graphene, and graphene was bonded into a 3-D structure by the solder-NPC, moreover, the KOH was an activator of NPC and also reacted with carbon atoms of GO to form holes in the carbonization process. The NPC/HG-2 showed the high specific surface area of 1135.3 m(2) g(-1), the rich hierarchical pore structure, and the high nitrogen doping amount of 6 at%. Used in the symmetric supercapacitor, the NPC/HG-2 exhibited the energy density of 29.33 Wh kg(-1) at a power density of 42.75 kW kg(-1), lower internal resistance and the excellent rate performance due to its unique internal pore structure. Moreover, the voltage of the NPC/HG-2 symmetric quasi-solid-state supercapacitor was up to 1.4 V.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据