METALS AND MATERIALS INTERNATIONAL
卷 27, 期 8, 页码 2645-2655出版社
KOREAN INST METALS MATERIALS
DOI: 10.1007/s12540-020-00611-1
关键词
Initial orientation; AZ80 magnesium alloy; Simulated body fluid; Corrosion behavior; Texture
资金
- National Natural Science Foundation of China [51775502, 51275472]
- Natural Science Foundation of Zhejiang Province [LY20E050024]
By investigating the corrosion behavior of different orientation samples of magnesium alloy immersed in simulated body fluid, it was found that the P-TD sample exhibited the best corrosion resistance, while the P-ND30 and P-ND60 samples showed similar corrosion behavior. A degradation evolution model was established, and the influence of initial orientation on corrosion behavior was discussed.
Three different orientation specimens (P-ND30, P-ND60 and P-TD) prepared from the rolled AZ80 magnesium alloy plates were immersed in simulated body fluid (SBF) for 384 h. Electrochemical impedance spectroscopy (EIS) tests were measured at 24 h, 96 h, 192 h, 288 h, and 384 h during immersion. The corrosion morphology and chemical composition of the three orientation specimens were investigated using scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). X-ray diffractometer (XRD) was used to evaluate the phase composition of the surface of the specimen at different immersion stages. The results indicated that the P-ND30 and P-ND60 specimens had similar corrosion behavior. The P-TD specimen showed the best corrosion resistance. A degradation evolution model was established, and the effect of initial orientation on corrosion behavior was discussed.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据