期刊
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE
卷 51, 期 5, 页码 2025-2034出版社
SPRINGER
DOI: 10.1007/s11661-020-05666-8
关键词
-
资金
- Advanced Steel Processing and Products Research Center (ASPPRC) at the Colorado School of Mines, Golden, CO, USA
- National Science Foundation division of Civil, Mechanical, and Manufacturing Innovation (NSF-CMMI) [1752530]
- Div Of Civil, Mechanical, & Manufact Inn
- Directorate For Engineering [1752530] Funding Source: National Science Foundation
Quenching and partitioning (Q&P) processing of third-generation advanced high strength steels generates multiphase microstructures containing metastable retained austenite. Deformation-induced martensitic transformation of retained austenite improves strength and ductility by increasing instantaneous strain hardening rates. This paper explores the influence of martensitic transformation and strain hardening on tensile performance. Tensile tests were performed on steels with nominally similar compositions and microstructures (11.3 to 12.6 vol. pct retained austenite and 16.7 to 23.4 vol. pct ferrite) at 980 and 1180 MPa ultimate tensile strength levels. For each steel, tensile performance was generally consistent along different orientations in the sheet relative to the rolling direction, but a greater amount of austenite transformation occurred during uniform elongation along the rolling direction. Neither the amount of retained austenite prior to straining nor the total amount of retained austenite transformed during straining could be directly correlated to tensile performance. It is proposed that stability of retained austenite, rather than austenite volume fraction, greatly influences strain hardening rate, and thus controls strength and ductility. If true, this suggests that tailoring austenite stability is critical for optimizing the forming response and crash performance of quenched and partitioned grades.