期刊
MATERIALS RESEARCH BULLETIN
卷 122, 期 -, 页码 -出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.materresbull.2019.110691
关键词
Sol-gel chemistry; Microporous materials; Crystal growth; Crystal structure; Catalytic properties
资金
- Fundamental Research Grant Scheme [203/PKIMIA/6711642, 203/PKIMIA/6711461]
- Malaysian Ministry of Higher Education
- USM Bridging Fund
Cs-ABW zeolite nanocrystals were synthesized using a microwave-assisted hydrothermal technique without an organic template. Using powder X-ray diffraction Rietveld refinement and spectroscopy, we found that pure ABW-type CsAlSiO4 zeolite nanocrystals (Si/Al ratio = 1.08) with an orthorhombic structure (space group Pc21n, a = 9.4425(21) angstrom; b = 5A437(11) angstrom; c = 8.9152(19) angstrom) can be crystallized from a clear precursor solution of 4SiO(2):1Al(2)O(3):16Cs(2)O:160H(2)O (180 degrees C, 6 min). The Cs-ABW nanoparticles had a mean particle size of 68 nm and were thermally and colloidally stable. The nanocrystals-which had high accessible basic sites, (Si-O-Al)Cs--(+), located at their external surface-were active in catalyzing the cyanoethylation of aliphatic alcohols under non-microwave instant heating, with 100 % selectivity to the desired product and high catalyst reusability. Furthermore, the cyanoethylation of methanol catalyzed by nanocrystalline Cs-ABW under instant heating had equal or better reactivity than those catalyzed by other solid base catalysts.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据