期刊
MATERIALS LETTERS
卷 258, 期 -, 页码 -出版社
ELSEVIER
DOI: 10.1016/j.matlet.2019.126806
关键词
Metals and alloys; High-entropy alloys; Nitrogen; Interstitial alloys; Microstructure; Precipitate
资金
- National Research Foundation of Korea (NRF) - Ministry of Education [NRF-2018R1A2B6005809]
- Ministry of Education and Science of the Russian Federation
- National Research Foundation of Korea [22A20130012792] Funding Source: Korea Institute of Science & Technology Information (KISTI), National Science & Technology Information Service (NTIS)
The precipitate formation and behavior in nitrogen-containing high-entropy alloy of equiatomic CoCrFeMnNi were characterized. The presence of 0.95 at.% nitrogen led to the formation of Cr2N precipitate in the as-recrystallized N-CoCrFeMnNi, in which annealing temperature affected the fraction and size of the formed Cr2N particles. It was observed that the Cr2N exhibited a Kikuchi crystal orientation relation (OR) with the face-centered cubic (FCC) matrix, and the OR was noticed to be in the plane of {1 1 1}gamma//{0 0 0 1}Cr2N and direction of < 1 1 0 >gamma//< 1 (1) over bar 00 > Cr2N. (C) 2019 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据