期刊
MATERIALS CHEMISTRY AND PHYSICS
卷 239, 期 -, 页码 -出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.matchemphys.2019.122077
关键词
Volcanic ash; GGBS; Structural geopolymers; Compressive strength; Setting time
资金
- Chinese Natural Science Fund [51262002, 21566006, 51561135012]
- Postdoctoral Project from the Fibre and Particle Engineering Research Unit, University of Oulu, Finland
This paper presents an investigation on the effect of ground granulated blast furnace slag on the geo-polymerization of low reactive volcanic ash. Volcanic ash was blended up to 50 wt% with slag at 10% intervals. The fresh geopolymer samples were cured at 25 and 60 degrees C for 3, 7 and 28 days. XRD, FTIR, TG and SEM were used for phases analysis. The results outlined that only 10 wt% of slag was enough to reduce the initial setting time of the geopolymer from more than 7 days to couple of hours (6.7 h). At 25 degrees C, the 28 days compressive strength increased with the addition of slag in the system until an optimum value of about 85 MPA. This strength development was suggested to arise from a synergetic formation of C-A-S-H/N-A-S-H geL At 60 degrees C, curing for periods longer than 7 days was not beneficial for strength development. These results are of interest for the valorization of low reactive volcanic ashes in the development of structural geopolymers, with related environmental and socioeconomic benefits.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据