期刊
JOURNAL OF THE MECHANICAL BEHAVIOR OF BIOMEDICAL MATERIALS
卷 103, 期 -, 页码 -出版社
ELSEVIER
DOI: 10.1016/j.jmbbm.2019.103515
关键词
POSS; Dental restorative composites; Low polymerization shrinkage; Double initiation system
资金
- National Natural Science Foundation of China [20974013, 51273017, 51403013, 51702076]
Polymerization shrinkage and mechanical properties affect the service life of dental restorative composites. Polyhedral oligomeric silsesquioxanes (POSS) can be an efficient strategy to improve the shrinkage properties and mechanical properties simultaneously. In this work, epoxycyclohexyl POSS (E-POSS) was used to modify the Bis-GMA/TEGDMA dental resins. E-POSS were introduced into the acrylic resin system via ring-opening reaction, and a cationic/free radical hybrid system was obtained. Double bond conversion, glass transition temperature, heterogeneity, crosslink density of dental resins and volumetric shrinkage, water sorption/solubility, flexural strength/modulus of dental composites were investigated. As the introduction of E-POSS caused higher double bond conversion and lower crosslink density, the polymerization shrinkage was significantly reduced to 2.91% (p < 0.05) and the flexural strength increased to 117.191V1Pa (p < 0.05) compared to the control sample (5.06%, 99.16 MPa, p<0.05). Lower water sorption and solubility were also observed in composites contained E-POSS (p < 0.05).
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据