JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
卷 40, 期 1, 页码 12-18出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.jeurceramsoc.2019.09.013
关键词
beta-SiAlON; Spark plasma sintering; Mechanical properties; Thermal conductivity
资金
- National Natural Science Foundation of China [51571144, 51701126, 21805196]
Fully dense beta-SiAlON ceramics with excellent mechanical properties and good thermal conductivity were fabricated by two-stage spark plasma sintering (SPS) processes without and with applying pressure respectively, using alpha-Si3N4 powder and 6 Al2O3-AlN-Y2O3 (in wt.%, label with 636), 424 and 422 additives. In the first stage SPS process without pressure, the relative dense beta-SiAlON ceramics with interlock microstructures of elongated grains and density of 3.14(similar to)3.18 g cm(-3), hardness of 14.00(similar to)14.82 GPa and fracture toughness of 6.00(similar to)6.63 MPa m(1/2) were obtained by sintering at about 1600 degrees C for 20 min. In the second stage SPS process at about 1425 degrees C for 5 min under pressure of 24 MPa, the fully dese beta-SiAlON ceramics with density of 3.2(similar to)3.24 g cm(-3), high hardness of 15.68(similar to)15.95 GPa, high fracture toughness of 6.38(similar to)7.03 MPa m(1/2) and thermal conductivity of 13.5 (similar to)19.6 Wm(-1) K-1 were obtained. The reaction between the samples and the graphite mold can be avoided in this fabrication method.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据