JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY
卷 94, 期 3, 页码 681-694出版社
SPRINGER
DOI: 10.1007/s10971-020-05216-z
关键词
Hydrothermal solution; Kinetics of orthosilicic acid polycondensation; Ultrafiltration membranes; Cryochemical vacuum sublimation; SiO2 sols; Gels; Nanopowders
Experiments were performed to obtain SiO2 sols, gels, and mesoporous nanopowders based on hydrothermal medium. To achieve this, polycondensation of orthosilicic acid (OSA) at certain pH and temperature, as well as ultrafiltration membrane concentration, sol-gel transition, and cryochemical vacuum sublimation were done. The dynamic light scattering, scanning and tunneling electron microscopy, low-temperature nitrogen adsorption, and others methods determined the physical and chemical characteristics of nanosized SiO2 samples. By choosing the pore size of the ultrafiltration membranes at the sol concentration stage, one can control the ratio of the SiO2 content to the total salt content and provide a zeta potential of nanoparticles sufficient for the stability of the sols. It was shown that by varying the temperature at the polycondensation stage from 20 to 90 degrees C at pH = 8.5-9.3, it is possible to control the final average diameter of SiO2 particles in the range from 5 to 100 nm, respectively. The specific surface area of particles are 50-500 m(2)/g, the average diameter of the mesoporous powders in the range of 2-15 nm; the fraction of the area (<4%) and volume (<0.25%) of micropores are low.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据