Sonochemical; Photolurninescence; Thermoluminescence; Photometric properties; Fingerprints
资金
- VGST [VGST/ICFIST-4/GRD-489]
Herein, we report hierarchical arrow-like structures of CaZrO3:Dy3+(1 - 11 mol %) are prepared by sonochemical route using bio template as a surfactant. High purity and crystallinity of the product was obtained in sonochemical route when compared to conventional methods. Morphological results showed arrow-like structures which are highly reliant on many experimental parameters such as, sonication time, bio-template concentration, sonication power, pH and surfactant to water ratio. The photoluminescence emission spectra consist of sharp peaks at similar to 481 nm (blue), 575 nm (yellow) and 665 nm (red), which ascribed to F-4(9/2) -> H-6(15/2), F-4(9/2) -> H-6(13/2) and F-4(9/2) -> H-6(11/2) transitions of Dy3+ ions, respectively. The decrement in the photoluminescence emission intensity after 7 mol % of Dy3+ ion concentration was clearly noticed, which may due to concentration quenching. The photometric properties of the prepared samples showed intense white emission with high color purity. Thermoluminescence glow curves of CaZrO3:Dy (3+) (7 mol %) showed broad and intense peak at similar to 143 degrees C at a warming rate of 2 degrees C s(-1). Thermoluminescence profile reveals the linear dependence with dose, least fading and highly reproducible. The optimized powders are employed to image the latent fingerprints with higher resolution on various porous, non-porous and semi-porous surfaces. The aforementioned results clearly indicate that the optimized hierarchical structures are effectively used in radiation dosimetry, display devices and advanced forensic applications.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据