The Ba0.85Ca0.15Zr0.1Ti0.9O3 (referred to as BCZT) ceramic powders were synthesized by the sol-gel method followed by calcining, and then the ceramics were obtained by sintering at different temperatures varied from 1200 to 1350 degrees C. The effects of sintering temperature on the microstructure, impedance spectroscopy, dielectric, and ferroelectric properties for BCZT ceramics have been thoroughly investigated. The pure perovskite structure and homogenous microstructure with high relative density (> 90%) for all BCZT ceramics are identified by XRD analysis and SEM measurement, and the stability is identified by the variable-temperature dielectric characterization. The impedance spectroscopy and well-defined polarization-electric field hysteresis loops for BCZT samples were detected at room temperature. In particular, the BCZT ceramic sintered at 1300 degrees C resulted the highest dielectric constant (epsilon(r) similar to 2170), the lowest dielectric loss (tan delta similar to 0.027), and the highest grain boundary resistance (R-gb similar to 8.9 x 10(7) Omega cm).
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据