JOURNAL OF MATERIALS PROCESSING TECHNOLOGY
卷 275, 期 -, 页码 -出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jmatprotec.2019.116383
关键词
Powder metallurgy high speed steel; Diffusion welding; Sparking plasma sintering; Tensile strength
资金
- National Natural Science Foundation of China [51771237, 51701023, 51704257]
- Scientific Research Fund of Hunan Provincial Education Department [16C0026]
- Hunan Provincial Key Laboratory of Materials Protection for Electric Power and Transportation [2016CL04]
- Changsha University of Science & Technology, China
A diffusion welding of HS 6-7-6-10-0.1LaB(6) powder metallurgy high speed steel (PMHSS) is successfully achieved by spark plasma sintering (SPS) for the first time in this research. The effect of welding process in terms of bonding temperature, pressure and time on microstructure evolution and tensile strength of the samples are studied in detail. Results indicate that the temperature plays a vital role on the welding quality. A complete welding can be obtained at 1100 degrees C within varied ranges of pressure and time. When welded at 1100 degrees C, 30 MPa for 30 min, the tensile strength of the sample after heat treatment reaches 2183.5 MPa, higher than that of the base material, which is further confirmed by the subgrain strengthening effect in SPS from TEM analysis.