期刊
JOURNAL OF HAZARDOUS MATERIALS
卷 384, 期 -, 页码 -出版社
ELSEVIER
DOI: 10.1016/j.jhazmat.2019.121485
关键词
Red mud; Activation process; Support; NiW/P-ARM nanocatalyst; Phosphorus promoter; Hydrodesulfurization reaction
The influence of phosphorus promoter addition on structural properties and hydrodesulfurization activity of NiW nanocatalysts supported on activated red mud, called NiW/P-ARM, was studied at atmospheric pressure. Before red mud usage, it was treated by Pratt and Christoverson technique and then NiW/P-ARM nanocatalysts with different phosphorus loadings were prepared by impregnation technique. The prepared samples were characterized by XRF, XRD, FESEM, BET, FTIR and H-2-TPR analyses. Base on the obtained results, XRF analysis indicated that activation process remarkably decreased Ca and Na content in the red mud. XRD results indicated the high dispersion of the tungstate, nickel and active phase (NiWO4) species on the surface of activated red mud support. FESEM analysis illustrated that all particles of NiW/P-ARM were less than 100 nm. TPR measurements revealed that phosphorus-promoted nanocatalysts had higher reduction potentials than nanocatalyst without promoter. The catalytic ability of synthesized nanocatalysts was investigated in a fixed bed reactor at atmospheric pressure and 380 degrees C using Iso diesel and light diesel as the reaction feeds. It was found that NiW/P-ARM with 1.5 wt.% prompter showed higher activity for hydrodesulfurization process and further addition of P promoter decreased the catalytic activity that may be due to the decrease in surface area or agglomeration particles.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据