期刊
JOURNAL OF ELECTROANALYTICAL CHEMISTRY
卷 859, 期 -, 页码 -出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jelechem.2020.113832
关键词
High temperature polymer electrolyte fuel cell; Phosphoric acid; Catalyst layer cracks; X-ray tomographic microscopy; Mitigating electrolyte losses; Lifetime
资金
- Impulsund Vemetzungsfonds der Helmholtz Gesellschaft [VH-NG-616]
Acid migration and loss at high current densities has previously been identified as an important degradation mechanism for phosphoric acid in high temperature polymer electrolyte fuel cells. In this process, the structure of the anode catalyst layer plays an important role for the acid migration mechanism. Therefore, the acid retaining capabilities of two significantly different catalyst layer structures were investigated by means of operando X-ray tomographic microscopy. In a commercial catalyst layer, with cracks with a mean width of 39 mu m, ideal crack connectivity and no bottlenecks in the crack structure, phosphoric acid penetrates and traverses the catalyst layer and migrates to the GDL and gas channel. In contrast, an in-house catalyst layer retained phosphoric acid within itself. Although with lower mean crack size of only 20 mu m, the different crack connectivity and accessibility, as determined by crack width and simulated mercury intrusion crack size analysis, were identified as main causes for better acid retaining capabilities. A fraction of over 95% of the crack-volume is protected by bottlenecks smaller than 20 mu m. The present analysis is a guideline for engineering acid retaining catalyst layers structures for high temperature polymer electrolyte fuel cells. (C) 2020 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据