Hydrogenation of TiO2 enhances its visible photoabsorption, leading to efficient photocatalytic activity. However, the role of hydrogen has not been fully understood. The anatase TiO2(101) surface treated by hydrogen ion irradiation at 500 eV was investigated by photoemission spectroscopy and nuclear reaction analysis. Hydrogen irradiation induces an in-gap state 1-1.6 eV below the Fermi level and a downward band bending of 0.27 eV. The H depth profile at 300 K shows a surface peak with an H amount of (2.9 +/- 0.3) x 10(15) cm(-2) with little concentration in a deeper region. At 200 K, on the other hand, the H depth profile shows a maximum at about 1 nm below the surface corresponding to an H amount of (6.1 +/- 0.3) x 10(15) cm(-2) along with a broad distribution extending to 50 nm at an average concentration of 0.8 at. %. These results show that H diffusion in anatase TiO2 is much faster than in rutile TiO2 [Y. Ohashi, J. Phys. Chem. C 123, 10319-10324 (2019)]. The H diffusion coefficient at 200 K is determined to be 2.7 +/- 0.1 x 10(-13) m(2) s(-1).
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据