INTERNATIONAL JOURNAL OF FATIGUE
卷 130, 期 -, 页码 -出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ijfatigue.2019.105232
关键词
Laser peening; Damage; Fatigue crack propagation; Crack closure; Crack arrest
资金
- National Science and Technology Major Project, China [2018ZX04005001]
- State Key Laboratory of Mechanical System and Vibration, China
This study investigates crack closure induced by laser peening (LP) and its effect on fatigue life extension of 2024-T351 aluminum alloy with initial fatigue crack. LP is applied directly in the initial fatigue crack region. This treatment leads to interesting observations of crack arrest that has not been reported before for LP, and significant fatigue life enhancement. The fatigue life of the LP-treated pre-cracked specimen is 412% and 44.7% higher than the untreated specimen and LP-treated specimen without pre-crack, respectively. The crack closure around the pre-crack resulting from the LP-induced plastic deformation is mainly responsible for fatigue life extension.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据