The metadynamic recrystallization (MDRX) of beta-solidified TiAl alloy and its effects on microstructural homogeneity were investigated in the present work. Based on the comprehensive microstructure characterizations in terms of scanning electron microscope in back-scattered electron (BSE) mode and electron back scattered diffraction (EBSD) technique, it is found that the occurrence of MDRX during the post-annealing process after hot compression leads to the decomposition of lamellar colonies, grain equalization and reduction of geometrically necessary dislocation. The MDRX in present alloy during interpass annealing process has a hardening effect on the subsequent flow behavior, while it is restricted due to the phase transformation gamma to alpha when annealing at 1200 degrees C. Moreover, the occurrence of MDRX can reduce the microstructure heterogeneity among various areas induced by the different strains and stain rates, thus, to result in the microstructural homogenization. Through investigating the MDRX behavior, the present work supports important information for optimizing forged microstructure of TiAl alloys.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据