期刊
EUROPEAN JOURNAL OF ORAL SCIENCES
卷 128, 期 1, 页码 81-88出版社
WILEY
DOI: 10.1111/eos.12668
关键词
fractographic analysis; fracture toughness; interface
资金
- Stick Tech LTD - Member of the GC Group
This study investigated the effect of discontinuous cellulose microfibers with various loading fractions on selected physical properties of glass polyalkenoate (glass ionomer) cement (GIC). Fiber-reinforced GIC (Exp-GIC) was prepared by adding discontinuous cellulose microfiber (with an average length of 500 mu m) at various mass ratios (1, 2, 3, 4, and 5 mass%) to the powder of conventional GIC (GC Fuji IX) using a high-speed mixing device. Fracture toughness, work of fracture, and compressive strength were determined for each experimental and control material. The specimens (n = 6) were wet stored (37 degrees C for 1 d) before testing. A scanning electron microscope equipped with an energy dispersive spectroscope was used to examine the surface of fibers after treatment with cement liquid. Data were analyzed using ANOVA. The Exp-GIC (5 mass%) specimen had statistically significantly higher fracture toughness (0.9 MPa.m(1/2)) than unreinforced material (0.4 MPa.m(1/2)). On the other hand, Exp-GIC with 1 mass% displayed the highest compressive strength (116 MPa) among all tested groups. The use of discontinuous cellulose microfibers with conventional GIC matrix considerably increased the toughening performance compared with the particulate GICs used.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据