CONSTRUCTION AND BUILDING MATERIALS
卷 238, 期 -, 页码 -出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.conbuildmat.2019.117719
关键词
Spectral induced polarization; Non-destructive technique; Alkali-silica reaction; Electrical double layer; Debye decomposition
资金
- Natural Sciences and Engineering Research Council (NSERC)
- Centre de Recherche sur les Infrastructures en Beton (CRIB)
- Fonds de recherche du Quebec -Nature et technologies (FRQNT)
The distress caused by alkali-silica reaction (ASR) to concrete structures can occur long time after the reaction has been triggered. We propose to use spectral induced polarization (SIP) as a non-destructive method for early detection of ASR reaction before the damage is apparent. Our research deals with monitoring the difference between the electrical behaviour (phase lag, bulk resistivity, relaxation time, total chargeability) of non-reactive (NR) and reactive (RC) concrete samples affected by ASR. Laboratory measurements of complex resistivity were done in the frequency range 1.43 mHz-20 kHz. A Debye decomposition (DD) model was used to determine the DC bulk resistivity (rho(0)), and the distribution of the chargeability as a function of the relaxation time. The total chargeability (Sigma(m)) and the mean relaxation time (tau(mean)) were computed as DD parameters to characterize the ASR development. While rho(0) was strongly dependent on the electrical conductivity of the solution (water, NaOH) with a constant change with time, both concrete mixtures saturated with the same solution showed an increase rho(0) due to the development of the matrix skeleton over time. In this work, rho(0) did not play a significant role to characterize the ASR development. For the samples affected by ASR, a significant evolution of Sigma(m) and tau(mean) was found compared to the non-affected mixtures (RC, NRC-H2O), specially over the low frequency range [1.48 mHz < f < 5.86 Hz]. The RC-NaOH samples displayed a strong linear correlation between normalized chargeabilty and imaginary conductivity. This observation could be associated with an increase in surface conductivity of the Stern layer at reactive grain surface or the evolution of specific surface area due to production of ASR silica gel, or both. Based on our conceptual electrochemical model of RTD presented in this work, an evolution of chargeability peak was observed at relatively long relaxation time tau > 10(2) s that could be associated with the polarization of aggregates affected by ASR. (C) 2019 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据