CONSTRUCTION AND BUILDING MATERIALS
卷 235, 期 -, 页码 -出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.conbuildmat.2019.117091
关键词
One-part AAM; Slag; Honeycomb ceramic; Compressive strength; Setting time
资金
- Jiangsu Higher Education Institutions for Priority Academic Program Development (PAPD)
A solid alkali source is a great choice to make one-part alkali activated materials (AAM). Conventional slag-based MM always suffer from short setting time and unsafe operation with liquid alkaline activators, thus restricting their usage in industry. This study aims to synthesize a new kind of one-part alkali-activated slag cement by using a porous honeycomb ceramic (HCC) as the carrier of sodium silicate activator. The solid activator was produced by making the honeycomb ceramic absorb water glass (Ms = 3.24, 8.21 wt% Na2O, 25.8%wt SiO2), drying for 5 h at 125 degrees C and then grinding it to powder with particle sizes between 10 and 50 pm. In this study, the result indicates that setting time of alkali activated slag cement (AASC) was successfully extended to at least 5 h by using the solid activator. The maximum compressive strength of the specimens made with 5% NaOH + 40% HCC and 6% NaOH + 40% HCC was similar to 40 MPa after 28 d of curing time. XRD (X-ray diffraction), FTIR (Fourier Transform infrared spectroscopy), SEM (Scanning Electron Microscope) and linear shrinkage analysis were applied in order to study the hydration product and the effect of the addition of HCC to the AASC. In terms of the strength properties and setting time, this one-part AASC could be classified as a Type 32.5 N and CEM IIIC class cement according to the European standard EN-197. (C) 2019 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据