COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING
卷 128, 期 -, 页码 -出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.compositesa.2019.105653
关键词
Biocomposites; Natural fibers; Environmental degradation; Mechanical properties
资金
- National Natural Science Foundation of China, China [51773048]
- Natural Science Foundation of Heilongjiang Province, China [E2017022]
- Fundamental Research Funds for the Central Universities [HEUCFP201724, HEUCFP201791]
In the current study, three different kinds of hemp fibre treated polybenzoxazine composites were exposed to accelerated weathering at 30 degrees C and 80% relative humidity (RH), till the saturated moisture uptake. The tensile, flexural, and impact properties of saturated samples were evaluated and results were compared with the unconditioned samples. The silane treated hemp fibre (STHF) composites showed the lowest decline in the properties. Afterwards, the STHF composites were exposed to various accelerated weathering conditions, in the range of 25-35 degrees C and 40-80% RH. Moisture uptake was slightly increased and tensile and flexural properties were gradually decreased as the exposure temperature and RH were increased. Highest decline was observed in the samples exposed at 35 degrees C and 80% RH. Furthermore, the slightly higher impact values were observed for the exposed composites. The composites colour was slightly lost and changes to lower shaded as the temperature and RH were raised.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据