Palladium nanopartides (PdNPs) were synthesized in a green way using sodium alginate functioning as both reductant and stabilizer. The formation of as-synthesized PdNPs was supervised by Ultraviolet-visible (UV-Vis) spectroscopy and confirmed by the surface plasmon resonance (SPR) band. The effect of several synthesis factors such as precursor ratio, solution pH, reaction time, and temperature were investigated by the factorial design of experiments in order to optimize the experimental conditions. The optimal synthesis parameters were achieved by heating 1.0 ml of 1.0% sodium alginate (SA), 3.0 ml of 10(-2) mol.L-1 H2PdCl4 at 80 degrees C for a period of 30 min in a neutral reaction medium (pH - 6). High-resolution transmission electron microscope (HRTEM), energy dispersive X-ray (EDX) spectroscopy, selected area electron diffraction (SAED) pattern, X-ray powder diffraction (XRD), and dynamic light scattering (DLS) were used to confirm the uniform spherical shapes and high crystallinity of PdNPs with average particle size of (2.12 +/- 1.42) nm. The SEM images show the distribution of PdNPs presented among the SA. MR spectra indicate that SA is a good capping agent to stabilize PdNPs for a long time. The catalytic degradation of model azo-clyes such as mono-azo (Cibacron Yellow FN-2R) and di-azo (Cibacron Deep Reel S-B) were confirmed the catalytic activity of PdNPs. The PdNPs can accelerate the degradation rate by more than 80 and 10 times respectively as confirmed by kinetics constant (k) values. (C) 2020 The Chemical Industry and Engineering Society of China, and Chemical Industry Press Co., Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据