CERAMICS INTERNATIONAL
卷 46, 期 8, 页码 10934-10941出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2020.01.108
关键词
SiC honeycomb/Al-Mg-Si composites; Wettability; Microstructure; Thermophysical properties
资金
- National Natural Science Foundation of China [51872222]
- Shaanxi Innovation Capacity Support Program [2018TD-031]
- Technology Innovation Leading Program of Shaanxi [2019QYPY-088]
- Open Project of the State Key Laboratory for Mechanical Behavior of Materials [20171903]
Directional SiC honeycomb/Al-Mg-Si composites with different Si alloying contents (2-12 wt%) were prepared by spontaneous infiltration. The effect of Si alloying content on the phase composition, microstructure and thermophysical properties of the composites were investigated. The results showed that the equilibrium contact angles between the SiC ceramic and different Al alloys were in the range of 60.5-72 degrees at 1273 K, benefitting the infiltration process. Meanwhile, the Si alloying content not only changed the phase composition of the composites, but also influenced the microstructure of the infiltrated Al alloys, especially changing the microstructure of Mg2Si phase from small flake-like eutectic phase (Mg2SiE) to large polygon-like primary phase (Mg2Sip). Due to the anisotropic feature of SiC honeycomb and the tunable phase composition and microstructure of the infiltrated Al alloys, the composites exhibited anisotropic and tailored thermophysical characteristics. The composites with the Si alloying content of 7 wt% possessed the optimum properties, with the highest TC of 140.95 W m(-1) K-1 in axial direction and relatively low CTE of 11.1 x 10(-6)/K in radial direction. Additionally, the reduction of anisotropy of composites' CTEs in two principal directions with the increase of Si alloying content was also discussed.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据