C/C composites; Biphase coating; Chemical vapor deposition; Microstructure; Anti-ablation performance
资金
- National Natural Science Foundation of China [51902242, 51672223, 51727804, 91860118, 51902010]
HfC-TaC and HfC-ZrC biphase coatings were synthesized on C/C composites through CVD technique with the aim of elevating the anti-ablation performance of the HfC monophase coating. The phase composition, microstructure and anti-ablation performance of the biphase coatings were researched, as well as the ablation mechanism of the coated C/C samples. Results manifested that both the HfC-TaC and HfC-ZrC coatings exhibited a compact and particle-stacked structure and combined well with the C/C substrate. Incorporating TaC is capable of enhancing the anti-ablation performance of the HfC coating by reason of forming the stable Hf6Ta2O17 phase during ablation. The evaporation and mechanical denudation of the Hf-Ta-O glassy film leaded to the HfC-TaC coating exfoliation. In comparison to the HfC and HfC-TaC coatings, the HfC-ZrC coating exhibited superior anti-ablation performance on account of the solid solution sintering between the HfO2 and ZrO2 particles and the good anti-scour performance of the oxide layer. After exposure to oxyacetylene torch for 120 s, the mass and linear ablation rates of the HfC-ZrC-coated C/C sample were only 0.63 mg/s and 0.21 mu m/s, respectively.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据