Inverse Growth of Large-Grain-Size and Stable Inorganic Perovskite Micronanowire Photodetectors

Control of forward and inverse reactions between perovskites and precursor materials is key to attaining high-quality perovskite materials. Many techniques focus on synthesizing nanostructured CsPbX3 materials (e.g., nanowires) via a forward reaction (CsX + PbX2 -> CsPbX3). However, low solubility of inorganic perovskites and complex phase transition make it difficult to realize the precise control of composition and length of nanowires using the conventional forward approach. Herein, we report the self-assembly inverse growth of CsPbBr3 micronanowires (MWs) (CsPb2 Br-5 -> CsPbBr3 + PbBr2 up arrow) by controlling phase transition from CsPb2Br5 to CsPbBr3. The two-dimensional (2D) structure of CsPb2 Br s serves as nucleation sites to induce initial CsPbBr3 MW growth. Also, phase transition allows crystal rearrangement and slows down crystal growth, which facilitates the MW growth of CsPbBr3 crystals along the 2D planes of CsPb2Br5. A CsPbBr3 MW photodetector constructed based on the inverse growth shows a high responsivity of 6.44 A W-1 and detectivity of similar to 10(12) Jones. Large grain size, high crystallinity, and large thickness can effectively alleviate decomposition/degradation of perovskites, which leads to storage stability for over 60 days in humid environment (relative humidity = 45%) and operational stability for over 3000 min under illumination (wavelength = 400 nm, light intensity = 20.06 mW cm(-2)).