MoS2; nanocomposite; hydrogel; radical initiation; self-healing
资金
- National Research Foundation of Korea (NRF) - Korea government (MSIT) [2019R1F1A1055458]
- National Research Foundation of Korea [2019R1F1A1055458] Funding Source: Korea Institute of Science & Technology Information (KISTI), National Science & Technology Information Service (NTIS)
This paper describes the multifunctional effect of molybdenum disulfide (MoS2) that enables the rapid and accessible preparation of nanocomposite hydrogels via a bottom-up design. The MoS2 nanoplatelet forms radical species through a redox reaction with persulfate under aqueous conditions while initiating the polymerization of acrylic monomers and providing noncovalent cross-linking points without requiring external stimuli or extra cross-linkers, leading to the formation of hydrogels that are in situ embedded with inorganic flakes. Furthermore, the addition of MoS2 could induce more rigid and elastic networks compared to those in control hydrogels using a typical cross-linker at the same level; for example, 0.08 wt % MoS2 resulted in a composite hydrogel of which the elastic modulus was 2.5 times greater than that from a hydrogel using N,N'-methylenebis(acrylamide) as the showing phase transition during polymerization. The composite hydrogels are self-healable, taking advantage of reversible physical cross-links. Thus, two cut hydrogel strips could be readily rejoined by heating at 70 degrees C, and the resulting whole strip showed mechanical strength similar to that of the pristine sample before it was cut. This synthetic approach would give way to the modular design of MoS2-containing composite hydrogels.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据