期刊
APPLIED SCIENCES-BASEL
卷 9, 期 20, 页码 -出版社
MDPI
DOI: 10.3390/app9204407
关键词
HKUST-1 MOF; carbon nanotubes; methylene blue; characterization; adsorption
类别
资金
- University of South Africa
Metal-organic frameworks (MOFs) (Hong Kong University of Science and Technology (HKUST)-1) have been widely studied using the hydrothermal method. Recently, efforts have also been geared toward the incorporation of multiwalled carbon nanotubes (MWCNTs) into the HKUST-1 MOF to advance its applications for gas storage as well as pollutant removal in wastewater. However, a significant reduction in the MWCNT/HKUST-1 composite surface area has limited its applications. We therefore synthesized HKUST-1 and HKUST-1 impregnated with acid-treated multiwalled carbon nanotubes (FMWCNTs). A large surface area of 1131.2 m(2)g(-1) was obtained after acid treatment of the as-received MWCNTs. HKUST-1 was found to have an average particle diameter of 6.5 to 8 mu m with a BET surface area of 1176.66 m(2)g(-1). The FMWCNT/HKUST-1 composites had a BET surface area of 1108.85 m(2)/g. The addition of FMWCNTs was found to increase the parent MOF pore volume from 0.76 to 1.93 cm(3)g(-1). A BJH desorption cumulative pore size of 6.97 nm was obtained in a composite sample. The maximum adsorption capacity of the composites was found to be greater than 100 mg/g at 298 K. The results obtained indicate that FMWCNT/HKUST-1 nanocomposites are a potential adsorbent for methylene blue (MB) removal in dye synthetic water.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据