期刊
METALS
卷 9, 期 10, 页码 -出版社
MDPI
DOI: 10.3390/met9101107
关键词
Ti-6Al-4V; Al; sliding; diffusion
资金
- National Key R&D Program of China [2018YFC1902401]
- National Natural Science Foundation of China [51671180, 51471159]
Elements' diffusion between Ti-6Al-4V alloy and Al in the process of sliding was investigated from 400 degrees C to 600 degrees C. The results showed that the atoms were diffused at the Ti-6Al-4V/Al interface. When sliding at 400 degrees C and 500 degrees C, no intermetallic compound was detected on the surface of Ti-6Al-4V alloy. When sliding at 600 degrees C, intermetallic TiAl3 was formed and grew on the surface of Ti-6Al-4V alloy. The diffusion thickness of Al atoms on the surface of Ti-6Al-4V alloy increased with increasing time and temperature. The diffusion kinetic equation of Al atoms on the surface of Ti-6Al-4V alloy was successfully established. The diffusion activation energy of Al atoms in the sliding process was calculated to be 28.22 kJ.mol(-1) and the dynamic index n was 0.5. The diffusion growth of Al atoms was controlled by normal parabolic law with time.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据