ACTA METALLURGICA SINICA-ENGLISH LETTERS
卷 33, 期 2, 页码 204-214出版社
CHINESE ACAD SCIENCES, INST METAL RESEARCH
DOI: 10.1007/s40195-019-00950-y
关键词
Stereolithography; Aluminum oxide; Sintering temperature; Shrinkage; 3D
In this work, aluminum oxide (Al2O3) ceramic samples were fabricated by 3D stereolithography printing. Printing process was followed by debinding and sintering. In addition, the effect of sintering temperature on microstructure and properties was investigated. Flexure strength was observed to increase with increasing sintering temperature due to fewer pores, fewer defects and stronger grain boundary bonding of samples at higher sintering temperatures. Maximum flexure strength of 138.5 MPa was obtained when sintering temperature was 150 degrees C. Furthermore, the shrinkage along length direction decreased with the decreasing sintering temperature until reaching minimum value of 1.02% after sintering at 1200 degrees C. After sintering at 1280 degrees C, flexure strength was 24.0 MPa and the shrinkage along length direction was 2.1%, which meets demands of ceramic core.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据